H11

Data Table for: Steel Grades : Tool Steel And Hard Alloy : H11

Chemical composition(mass fraction)(wt.%)

  • C
  • Si
  • Mn
  • P
  • S
  • Cr
  • Mo
  • V
  • 0.33～0.43
  • 0.80～1.20
  • 0.20～0.50
  • ≤0.030
  • ≤0.030
  • 4.75～5.50
  • 1.10～1.60
  • 0.30～0.60

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

√

√

√

√

√

Can produce H11 specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • H11
  • H11
  • H11
  • H11
  • H11
  • H11
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

Alloy tool steel Annealing hardness HBS: 235
Cold pull hardness HBS: 262
Preheat temperature / ℃ : 788
Quenching temperature / ℃ | salt bath furnaces: 996
Quenching temperature / ℃ | controlled atmosphere furnace: 1010
Holding time/min: 5 to 15
Quenching medium: air cold
Tempering temperature / ℃ : 552
After tempering quartile hardness HRC: 53

Standard download

ASTM H11 PDF
ASTM H11 Word

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:H11

Previous pageH10
Next page:T20811

Further reading: