ASTM 1017
Data Table for: Steel Grades : Structure Steel : ASTM 1017
Chemical composition(mass fraction)(wt.%)
- C
- Mn
- P
- S
- 0.15～0.20
- 0.30～0.60
- ≤0.040
- ≤0.050
Mechanical Properties
- Quantity
- Value
- Unit
- Young's modulus
- Tensile strength
- Elongation
- Fatigue
- Yield strength
- 200000 - 200000
- 650 - 880
- 8 - 25
- 275 - 275
- 350 - 550
- MPa
- MPa
- %
- MPa
- MPa
Physical Properties
- Quantity
- Value
- Unit
- Thermal expansion
- Thermal conductivity
- Specific heat
- Melting temperature
- Density
- Resistivity
- 10 - 10
- 25 - 25
- 460 - 460
- 1450 - 1510
- 7700 - 7700
- 0.55 - 0.55
- e-6/K
- W/m.K
- J/kg.K
- °C
- kg/m3
- Ohm.mm2/m
Heat Treatment:
Annealing |
Quenching |
Tempering |
Normalizing |
Q & T |
√ |
√ |
√ |
√ |
√ |
Can produce ASTM 1017 specifications and size
- Steel grade
- Specification
- Processing range(mm)
- ASTM 1017
- ASTM 1017
- ASTM 1017
- ASTM 1017
- ASTM 1017
- ASTM 1017
- Φ1 to Φ2000
- 10 to 1000
- 0.08 to 800(T)*10 to 1500(W)*Long
- Pipe/tube/slugs/donuts/cubes/other shapes
- OD: Φ4-410; WT: 1-35 mm
- THK:0.1mm Width:1500mm
Description
General use carbon steel bar Note: 1. ASTM standard quality level of carbon steel rod can see ASTM cold A108-1999, its GangHao the chemical composition of the same with this form.
2. ASTM special levels of quality carbon steel rod can see the hot working ASTM A576 (90 b) (2000), the GangHao the chemical composition of the same with this form.
3. Require Si content (mass fraction), usually in the following 4 files a choice: 0.10% or Si, Si 0.10 ~ 0.20%, Si 0.20 ~ 0.40%, Si 0.30 ~ 0.60%.
4. Require Cu content (quality score) is 0.20% or Cu.
2. ASTM special levels of quality carbon steel rod can see the hot working ASTM A576 (90 b) (2000), the GangHao the chemical composition of the same with this form.
3. Require Si content (mass fraction), usually in the following 4 files a choice: 0.10% or Si, Si 0.10 ~ 0.20%, Si 0.20 ~ 0.40%, Si 0.30 ~ 0.60%.
4. Require Cu content (quality score) is 0.20% or Cu.
Standard download
Click the Get Adobe Reader button to download the Adobe Reader:
Related steel grade search:ASTM 1017
Previous pageUNS G10170
Next page:ASTM 1018