M261
Data Table for: Steel Grades : Mould Steel : M261
Chemical composition(mass fraction)(wt.%)
Mechanical Properties
- Quantity
- Value
- Unit
- Young's modulus
- Tensile strength
- Elongation
- Fatigue
- Yield strength
- 200000 - 200000
- 650 - 880
- 8 - 25
- 275 - 275
- 350 - 550
- MPa
- MPa
- %
- MPa
- MPa
Physical Properties
- Quantity
- Value
- Unit
- Thermal expansion
- Thermal conductivity
- Specific heat
- Melting temperature
- Density
- Resistivity
- 10 - 10
- 25 - 25
- 460 - 460
- 1450 - 1510
- 7700 - 7700
- 0.55 - 0.55
- e-6/K
- W/m.K
- J/kg.K
- °C
- kg/m3
- Ohm.mm2/m
Heat Treatment:
Annealing |
Quenching |
Tempering |
Normalizing |
Q & T |
√ |
√ |
√ |
√ |
√ |
Can produce M261 specifications and size
- Steel grade
- Specification
- Processing range(mm)
- M261
- M261
- M261
- M261
- M261
- M261
- Φ1 to Φ2000
- 10 to 1000
- 0.08 to 800(T)*10 to 1500(W)*Long
- Pipe/tube/slugs/donuts/cubes/other shapes
- OD: Φ4-410; WT: 1-35 mm
- THK:0.1mm Width:1500mm
Description
|
Physical Properties
|
Metric
|
English
|
Comments
|
|
Density
|
7.82g/cc
|
0.283 lb/in³
|
|
|
|
|||
|
Mechanical Properties
|
Metric
|
English
|
Comments
|
|
Hardness, Rockwell C
|
30.0
|
30.0
|
Solution Annealed
|
|
|
38.0 - 42.0
|
38.0 - 42.0
|
Stock Standard
|
|
|
<= 44.0
|
<= 44.0
|
After Aging
|
|
Modulus of Elasticity
|
210GPa
|
30500 ksi
|
|
|
|
|||
|
Thermal Properties
|
Metric
|
English
|
Comments
|
|
CTE, linear
|
11.3 µm/m-°C
@Temperature 100 °C |
6.28 µin/in-°F
@Temperature 212 °F |
|
|
|
12.2 µm/m-°C
@Temperature 200 °C |
6.78 µin/in-°F
@Temperature 392 °F |
|
|
|
12.8 µm/m-°C
@Temperature 300 °C |
7.11 µin/in-°F
@Temperature 572 °F |
|
|
|
13.2 µm/m-°C
@Temperature 400 °C |
7.33 µin/in-°F
@Temperature 752 °F |
|
|
|
13.5 µm/m-°C
@Temperature 500 °C |
7.50 µin/in-°F
@Temperature 932 °F |
|
|
Thermal Conductivity
|
25.0 W/m-K
@Temperature 20.0 °C |
174 BTU-in/hr-ft²-°F
@Temperature 68.0 °F |
|
|
|
26.4 W/m-K
@Temperature 100 °C |
183 BTU-in/hr-ft²-°F
@Temperature 212 °F |
|
|
|
29.5 W/m-K
@Temperature 200 °C |
205 BTU-in/hr-ft²-°F
@Temperature 392 °F |
|
|
|
31.5 W/m-K
@Temperature 300 °C |
219 BTU-in/hr-ft²-°F
@Temperature 572 °F |
|
|
|
32.3 W/m-K
@Temperature 400 °C |
224 BTU-in/hr-ft²-°F
@Temperature 752 °F |
|
|
|
|||
|
Component Elements Properties
|
Metric
|
English
|
Comments
|
|
Aluminum, Al
|
1.20 %
|
1.20 %
|
|
|
Carbon, C
|
0.130 %
|
0.130 %
|
|
|
Chromium, Cr
|
0.350 %
|
0.350 %
|
|
|
Copper, Cu
|
1.20 %
|
1.20 %
|
|
|
Iron, Fe
|
91.32 %
|
91.32 %
|
As Balance
|
|
Manganese, Mn
|
2.00 %
|
2.00 %
|
|
|
Nickel, Ni
|
3.50 %
|
3.50 %
|
|
|
Silicon, Si
|
0.300 %
|
0.300 %
|
|