DC53
Data Table for: Steel Grades : Mould Steel : DC53
Chemical composition(mass fraction)(wt.%)
Mechanical Properties
- Quantity
- Value
- Unit
- Young's modulus
- Tensile strength
- Elongation
- Fatigue
- Yield strength
- 200000 - 200000
- 650 - 880
- 8 - 25
- 275 - 275
- 350 - 550
- MPa
- MPa
- %
- MPa
- MPa
Physical Properties
- Quantity
- Value
- Unit
- Thermal expansion
- Thermal conductivity
- Specific heat
- Melting temperature
- Density
- Resistivity
- 10 - 10
- 25 - 25
- 460 - 460
- 1450 - 1510
- 7700 - 7700
- 0.55 - 0.55
- e-6/K
- W/m.K
- J/kg.K
- °C
- kg/m3
- Ohm.mm2/m
Heat Treatment:
Annealing |
Quenching |
Tempering |
Normalizing |
Q & T |
√ |
√ |
√ |
√ |
√ |
Can produce DC53 specifications and size
- Steel grade
- Specification
- Processing range(mm)
- DC53
- DC53
- DC53
- DC53
- DC53
- DC53
- Φ1 to Φ2000
- 10 to 1000
- 0.08 to 800(T)*10 to 1500(W)*Long
- Pipe/tube/slugs/donuts/cubes/other shapes
- OD: Φ4-410; WT: 1-35 mm
- THK:0.1mm Width:1500mm
Description
|
Physical Properties
|
Metric
|
English
|
Comments
|
|
Specific Gravity
|
7.87g/cc
|
7.87g/cc
|
|
|
|
|||
|
Mechanical Properties
|
Metric
|
English
|
Comments
|
|
Hardness, Rockwell C
|
62.0 - 63.0
|
62.0 - 63.0
|
|
|
Tensile Strength, Ultimate
|
2750 MPa
|
398000 psi
|
when tempered at 175-300°C
|
|
Modulus of Elasticity
|
150 GPa
|
21700ksi
|
|
|
Poissons Ratio
|
0.280
|
0.280
|
|
|
Fatigue Strength
|
8 MPa
@# of Cycles 1.00e+6 |
121000 psi
@# of Cycles 1.00e+6 |
Heat treatment: 1030°C, 520°C (x2), HRc63
|
|
Shear Modulus
|
58.5 GPa
|
8480 ksi
|
Modulus of Rigidity
|
|
|
|||
|
Thermal Properties
|
Metric
|
English
|
Comments
|
|
CTE, linear
|
12.2 µm/m-°C
@Temperature -100 °C |
6.78µin/in-°F
@Temperature -148 °F |
|
|
|
12.3 µm/m-°C
@Temperature 300 °C |
6.83µin/in-°F
@Temperature 572 °F |
|
|
|
13.2 µm/m-°C
@Temperature 500 °C |
7.33 µin/in-°F
@Temperature 932 °F |
|
|
Thermal Conductivity
|
23.8 W/m-K
|
165 BTU-in/hr-ft²-°F
|
RT
|
|
25.1 W/m-K
@Temperature 100 °C |
174 BTU-in/hr-ft²-°F
@Temperature 212 °F |
||
|
|
27.2 W/m-K
@Temperature 400 °C |
188 BTU-in/hr-ft²-°F
@Temperature 752 °F |
|
Standard download
Click the Get Adobe Reader button to download the Adobe Reader:
Related steel grade search:DC53