SAE J403

Data Table for: Steel Grades : Carbon Steel : SAE J403

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

√

√

√

√

√

Can produce SAE J403 specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • SAE J403
  • SAE J403
  • SAE J403
  • SAE J403
  • SAE J403
  • SAE J403
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

Categories: Metal; Ferrous Metal; Carbon Steel; AISI 1000 Series Steel; Low Carbon steel

Material Notes: AISI 1005 Low Carbon steel

Key Words: UNS G10050, ASTM A29, ASTM A510, MIL SPEC MIL-S-11310 (CS1005), SAE J403, SAE J412

 

 

Physical Properties Metric English Comments
Density  7.872 g/cc 0.2844 lb/in³ Composition 0.06% C, 0.38% Mn, 0.01% Si, annealed at 925°C
 
Mechanical Properties Metric English Comments
Modulus of Elasticity  200 GPa 29000 ksi Typical for steel
Bulk Modulus  140 GPa 20300 ksi Typical for steel
Poissons Ratio  0.290 0.290 Typical For steel
Shear Modulus  80.0 GPa 11600 ksi Typical for steel
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000174 ohm-cm 0.0000174 ohm-cm Typical steel
 
Thermal Properties Metric English Comments
CTE, linear 12.6 µm/m-°C
@Temperature 0.000 - 100 °C		 7.00 µin/in-°F
@Temperature 32.0 - 212 °F
  13.1 µm/m-°C
@Temperature 0.000 - 200 °C		 7.28 µin/in-°F
@Temperature 32.0 - 392 °F
  13.5 µm/m-°C
@Temperature 0.000 - 300 °C		 7.50 µin/in-°F
@Temperature 32.0 - 572 °F
  13.7 µm/m-°C
@Temperature 0.000 - 400 °C		 7.61 µin/in-°F
@Temperature 32.0 - 752 °F
  13.7 µm/m-°C
@Temperature 0.000 - 1000 °C		 7.61 µin/in-°F
@Temperature 32.0 - 1830 °F
  14.2 µm/m-°C
@Temperature 0.000 - 500 °C		 7.89 µin/in-°F
@Temperature 32.0 - 932 °F
  14.6 µm/m-°C
@Temperature 0.000 - 600 °C		 8.11 µin/in-°F
@Temperature 32.0 - 1110 °F
  14.9 µm/m-°C
@Temperature 0.000 - 700 °C		 8.28 µin/in-°F
@Temperature 32.0 - 1290 °F
  16.6 µm/m-°C
@Temperature 0.000 - 800 °C		 9.22 µin/in-°F
@Temperature 32.0 - 1470 °F
Specific Heat Capacity  0.481 J/g-°C 0.115 BTU/lb-°F 50-100°C (122-212°F)
  0.519 J/g-°C
@Temperature 150 - 200 °C		 0.124 BTU/lb-°F
@Temperature 302 - 392 °F
  0.536 J/g-°C
@Temperature 200 - 250 °C		 0.128 BTU/lb-°F
@Temperature 392 - 482 °F
  0.553 J/g-°C
@Temperature 250 - 300 °C		 0.132 BTU/lb-°F
@Temperature 482 - 572 °F
  0.595 J/g-°C
@Temperature 350 - 400 °C		 0.142 BTU/lb-°F
@Temperature 662 - 752 °F
  0.662 J/g-°C
@Temperature 450 - 500 °C		 0.158 BTU/lb-°F
@Temperature 842 - 932 °F
  0.754 J/g-°C
@Temperature 550 - 600 °C		 0.180 BTU/lb-°F
@Temperature 1020 - 1110 °F
  0.846 J/g-°C
@Temperature 850 - 900 °C		 0.202 BTU/lb-°F
@Temperature 1560 - 1650 °F
  0.867 J/g-°C
@Temperature 650 - 700 °C		 0.207 BTU/lb-°F
@Temperature 1200 - 1290 °F
  1.105 J/g-°C
@Temperature 700 - 750 °C		 0.2641 BTU/lb-°F
@Temperature 1290 - 1380 °F
 
Component Elements Properties Metric English Comments
Carbon, C  <= 0.060 % <= 0.060 %
Iron, Fe  99.5 - 100 % 99.5 - 100 % As remainder
Manganese, Mn  <= 0.35 % <= 0.35 %
Phosphorous, P  <= 0.040 % <= 0.040 %
Sulfur, S  <= 0.050 % <= 0.050 %

Standard download

SAE J403 PDF
SAE J403 Word

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:SAE J403

Previous page1.0037
Next page:UNS G10100

Further reading: