ASTM A36
Data Table for: Steel Grades : Carbon Steel : ASTM A36
Chemical composition(mass fraction)(wt.%)
Mechanical Properties
- Quantity
- Value
- Unit
- Young's modulus
- Tensile strength
- Elongation
- Fatigue
- Yield strength
- 200000 - 200000
- 650 - 880
- 8 - 25
- 275 - 275
- 350 - 550
- MPa
- MPa
- %
- MPa
- MPa
Physical Properties
- Quantity
- Value
- Unit
- Thermal expansion
- Thermal conductivity
- Specific heat
- Melting temperature
- Density
- Resistivity
- 10 - 10
- 25 - 25
- 460 - 460
- 1450 - 1510
- 7700 - 7700
- 0.55 - 0.55
- e-6/K
- W/m.K
- J/kg.K
- °C
- kg/m3
- Ohm.mm2/m
Heat Treatment:
Annealing |
Quenching |
Tempering |
Normalizing |
Q & T |
√ |
√ |
√ |
√ |
√ |
Can produce ASTM A36 specifications and size
- Steel grade
- Specification
- Processing range(mm)
- ASTM A36
- ASTM A36
- ASTM A36
- ASTM A36
- ASTM A36
- ASTM A36
- Φ1 to Φ2000
- 10 to 1000
- 0.08 to 800(T)*10 to 1500(W)*Long
- Pipe/tube/slugs/donuts/cubes/other shapes
- OD: Φ4-410; WT: 1-35 mm
- THK:0.1mm Width:1500mm
Description
ASTM A36, >8 to 15 in. thick, as-rolled steel plate
Categories: Metal; Ferrous Metal; ASTM Steel; Carbon Steel; Low Carbon steel
Material Notes: A popular "workhorse" grade, it is used widely for various applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.85 g/cc | 0.284 lb/in³ | Typical of ASTM steel |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 119 - 159 | 119 - 159 | based on conversion from tensile strength |
| Hardness, Rockwell B | 67.0 - 83.0 | 67.0 - 83.0 | based on conversion from tensile strength |
| Tensile Strength at Break | 400 - 552 MPa | 58000 - 80000 psi | |
| Tensile Strength, Yield | >= 221 MPa | >= 32000 psi | |
| Elongation at Break | >= 18.0 % | >= 18.0 % | in 8" |
| >= 21.0 % | >= 21.0 % | in 2", > 24" W | |
| Bend Radius, Minimum | 0.500 t | 0.500 t | ≤3/4" W; ASTM A6 PARA. S14 |
| 1.00 t | 1.00 t | >3/4 to 1" W; ASTM A6 PARA. S14 | |
| 1.50 t | 1.50 t | >1 to 1-1/2" W; ASTM A6 PARA. S14 | |
| 2.50 t | 2.50 t | >1-1/2 to 2" W; ASTM A6 PARA. S14 | |
| 3.00 t | 3.00 t | >2" W; ASTM A6 PARA. S14 | |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | <= 0.290 % | <= 0.290 % | |
| Copper, Cu | >= 0.020 % | >= 0.020 % | |
| Iron, Fe | >= 98.0 % | >= 98.0 % | |
| Manganese, Mn | 0.85 - 1.20 % | 0.85 - 1.20 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | 0.15 - 0.40 % | 0.15 - 0.40 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |