AMS 4924

Data Table for: Steel Grades : Carbon Steel : AMS 4924

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

√

√

√

√

√

Can produce AMS 4924 specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • AMS 4924
  • AMS 4924
  • AMS 4924
  • AMS 4924
  • AMS 4924
  • AMS 4924
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

AISI 1010 steel, hot rolled bar, 19-32 mm (0.75-1.25 in) round or thickness
Categories: Metal; Ferrous Metal; Carbon Steel; AISI 1000 Series Steel; Low Carbon steel
Material Notes: Easily cold formed by heading, extruding, upsetting, bending, and other deforming processes. Uses for wires include electroplated products, such as racks, storage bins, shopping carts, fan guards, and jewelry, and unplated such as wires, staples, hardware, and barbed wire.
Key Words: UNS G10100, AMS 5040, AMS 5042, AMS 5044, AMS 5047, AMS 5053, ASTM A29, ASTM A108, ASTM A510, ASTM A519, ASTM A545, ASTM A549, ASTM A575, ASTM A576, MIL SPEC MIL-S-11310 (CS1010), JIS S 9 CK, SAE J403, SAE J412, SAE J414, DIN 1.1121, AFNOR XC 10 (Fr), JIS S10 C, JIS S 12 C

 

 

Physical Properties Metric English Comments
Density  7.87 g/cc 0.284 lb/in³ Typical for steel
 
Mechanical Properties Metric English Comments
Hardness, Brinell  95 95
Hardness, Knoop  113 113 Converted from Brinell hardness.
Hardness, Rockwell B  55 55 Converted from Brinell hardness.
Hardness, Vickers  98 98 Converted from Brinell hardness.
Tensile Strength, Ultimate  325 MPa 47100 psi
Tensile Strength, Yield  180 MPa 26100 psi
Elongation at Break  28.0 % 28.0 % in 50 mm
Reduction of Area  50.0 % 50.0 %
Modulus of Elasticity  200 GPa 29000 ksi Typical for steel
Bulk Modulus  140 GPa 20300 ksi Typical for steel
Poissons Ratio  0.290 0.290 Typical For Steel
Machinability  55 % 55 % Based on AISI 1212 steel. as 100% machinability. The machinability of Group I bar, rod, and wire products can be improved by cold drawing.
Shear Modulus  80.0 GPa 11600 ksi Typical for steel
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000143 ohm-cm 0.0000143 ohm-cm condition unknown
 
Thermal Properties Metric English Comments
CTE, linear 12.2 µm/m-°C
@Temperature 0.000 - 100 °C		 6.78 µin/in-°F
@Temperature 32.0 - 212 °F
  13.0 µm/m-°C
@Temperature 0.000 - 200 °C		 7.22 µin/in-°F
@Temperature 32.0 - 392 °F
  13.5 µm/m-°C
@Temperature 0.000 - 300 °C		 7.50 µin/in-°F
@Temperature 32.0 - 572 °F
  13.8 µm/m-°C
@Temperature 0.000 - 400 °C		 7.67 µin/in-°F
@Temperature 32.0 - 752 °F
  14.2 µm/m-°C
@Temperature 0.000 - 500 °C		 7.89 µin/in-°F
@Temperature 32.0 - 932 °F
  14.6 µm/m-°C
@Temperature 0.000 - 600 °C		 8.11 µin/in-°F
@Temperature 32.0 - 1110 °F
  14.9 µm/m-°C
@Temperature 0.000 - 700 °C		 8.28 µin/in-°F
@Temperature 32.0 - 1290 °F
Specific Heat Capacity  0.448 J/g-°C 0.107 BTU/lb-°F condition unknown; 50-100°C (122-212°F)
  0.498 J/g-°C
@Temperature 150 - 200 °C		 0.119 BTU/lb-°F
@Temperature 302 - 392 °F
  0.519 J/g-°C
@Temperature 200 - 250 °C		 0.124 BTU/lb-°F
@Temperature 392 - 482 °F
  0.536 J/g-°C
@Temperature 250 - 300 °C		 0.128 BTU/lb-°F
@Temperature 482 - 572 °F
  0.565 J/g-°C
@Temperature 300 - 350 °C		 0.135 BTU/lb-°F
@Temperature 572 - 662 °F
  0.590 J/g-°C
@Temperature 350 - 400 °C		 0.141 BTU/lb-°F
@Temperature 662 - 752 °F
  0.649 J/g-°C
@Temperature 400 - 450 °C		 0.155 BTU/lb-°F
@Temperature 752 - 842 °F
  0.729 J/g-°C
@Temperature 550 - 600 °C		 0.174 BTU/lb-°F
@Temperature 1020 - 1110 °F
  0.825 J/g-°C
@Temperature 650 - 700 °C		 0.197 BTU/lb-°F
@Temperature 1200 - 1290 °F
Thermal Conductivity  51.9 W/m-K 360 BTU-in/hr-ft²-°F Typical steel
 
Component Elements Properties Metric English Comments
Carbon, C  0.080 - 0.13 % 0.080 - 0.13 %
Iron, Fe  99.18 - 99.62 % 99.18 - 99.62 % As remainder
Manganese, Mn  0.30 - 0.60 % 0.30 - 0.60 %
Phosphorous, P  <= 0.040 % <= 0.040 %
Sulfur, S  <= 0.050 % <= 0.050 %

Users viewing this material also viewed the following:
AISI 1010 Steel, cold drawn
AISI 1010 Steel, cold drawn bar, 19-32 mm (0.75-1.25 in) round or thickness
AISI 1010 Steel, CQ sheet,1.6-5.8 mm round or thickness
AISI 1008 Steel, hot rolled bar, 19-32 mm (0.75-1.25 in) round
AISI 1008 Steel, cold drawn bar, 19-32 mm (0.75-1.25 in) round

M1010B / 6783

Standard download

AMS 4924 PDF
AMS 4924 Word

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader